Assembly adhesive FIX2 GT 290 ml white

Tytan Professional HIGH TACK Express is an adhesive based on the latest generation of hybrid polymers

with fast initial grab and accelerated curing.

Creates a very strong bond that can be loaded after approximately 30 minutes,

and reaches full strength after approximately 3 hours.

The resulting joint provides excellent vibration damping and resists changing weather conditions, UV radiation and diluted chemicals.

The product is chemically neutral, contains no solvents or isocyanates, does not corrode metals and does not damage sensitive surfaces.

Application

-bonding a wide range of finishing materials to typical surfaces such as concrete, plaster, chipboard,

wood, brick, glass, mirror, expanded polystyrene; bonding wall trims, plinths, thresholds, panels and ceramic tiles

-bonding decorative components made of wood, cork, chipboard, metal, stone, laminates, expanded polystyrene and marble

-bonding mirrors

-flexible joining of components in structures subject to vibration

-bonding components and materials such as:

wood, glass, mirrors (including lacquered mirrors), expanded polystyrene, metal, PVC, gypsum, plasterboard, stainless steel, zinc-plated steel,

artificial and natural stone, concrete, brick, cork, ceramics, porcelain, mirrors,

mineral wool and glass wool - in any combination,

bonding decorative components, hobby work, minor repairs.

Bonding furniture (including garden furniture), bent components, drainpipes, sanitary fittings and components of structures

outside building construction, e.g. in trailers, semitrailers and containers (including refrigerated containers), etc., minor roof repairs

Technical parameters

colour: white

consistency: thick paste

initial curing time: 30 min.*

working time 5-10 min.

temperature resistance (after curing): from -40°C to +90°C

application temperature from +5°C to +40°C

tool cleaning: acetone, extraction naphtha

full curing time: 3 h*

stress at break (ISO 37): 4 MPa

initial adhesion: 200 kg / m2 (after 5 seconds)

* Measured at a temperature of 23 and relative humidity of 50 %. Lower temperature and humidity and greater joint thickness extend curing time.